Metals -> High-temperature or heat-resistant steel and alloy -> Relaxation-resistant steel Characteristics of the material 20KHMFBR ( 20HMFBR, 20ÕÌÔÁÐ ).
Material : 20KHMFBR ( 20HMFBR, 20ÕÌÔÁÐ ) Classification : Relaxation-resistant steel
Chemical composition in % of the material 20KHMFBR ( 20HMFBR, 20ÕÌÔÁÐ ) . C Si Mn Ni S P Cr Mo V Nb Cu B 0.17 - 0.26 max 0.37 0.5 - 0.8 max 0.45 max 0.03 max 0.03 1 - 1.5 0.8 - 1.1 0.7 - 1 max 0.15 max 0.2 max 0.005
Temperature of critical points of the grade 20KHMFBR ( 20HMFBR, 20ÕÌÔÁÐ ).
Ac1 = 810 , Ac3 (Acm ) = 950 , Ar3 (Arcm ) = 800 , Ar1 = 690
Mechanical properties under Ò=20o Ñ of the material 20KHMFBR ( 20HMFBR, 20ÕÌÔÁÐ ) .
Assortment
Dimension
Direct.
s â
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - Bar longitudinal 900 15 55 400 Normalizing 1100o C,Drawing 730o C, 5h, 1076 958 13.3 46.6 150 Normalizing 1100o C,Drawing 650o C, 6h,
Physical properties of the material 20KHMFBR ( 20HMFBR, 20ÕÌÔÁÐ ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 2.17 7900 100 2.11 41 200 2.05 46.1 300 1.96 48.2 400 1.88 50.2 500 1.8 52.8 600 1.67 54.4 700 1.52 56.1 T E 10- 5 a 10 6 l r C R 10 9
Specification :
Mechanical properties :
s â - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Èíôîðìàöèÿ âçÿòà ñ ñàéòà Ìàðî÷íèê ñòàëè è ñïëàâîâ
© 2002 - 2009 Ìîññïåöñòàëü. Âñå ïðàâà çàùèùåíû