Characteristics of the material 08KH17N13M2T ( 08H17N13M2T, 08Х17Н13М2Т ).
Material :
08KH17N13M2T ( 08H17N13M2T, 08Х17Н13М2Т )
Substitute:
10Х17Н13М2Т
Classification :
Corrosion-resistant steel for general purposes
Chemical composition in % of the material 08KH17N13M2T ( 08H17N13M2T, 08Х17Н13М2Т ) .
C
Si
Mn
Ni
S
P
Cr
Mo
Cu
-
max 0.08
max 0.8
max 2
12 - 14
max 0.02
max 0.035
16 - 18
2 - 3
max 0.3
(5 С - 0.7) Ti, остальное Fe
Mechanical properties under Т=20oС of the material 08KH17N13M2T ( 08H17N13M2T, 08Х17Н13М2Т ) .
Assortment
Dimension
Direct.
sв
sT
d5
y
KCU
Heat treatment
-
mm
-
MPa
MPa
%
%
kJ / m2
-
Bar
Ж 60
490
196
40
50
Guenching 1050 - 1100oC,
Sheet trick
510
196
40
Guenching 1030 - 1080oC,Cooling air,
Technological properties of the material 08KH17N13M2T ( 08H17N13M2T, 08Х17Н13М2Т ) .
Weldability:
without limitations.
Specification :
Mechanical properties :
sв
- Tensile strength , [MPa]
sT
- Yield stress, [MPa]
d5
- Specific elongation at fracture , [ % ]
y
- Reduction of area , [ % ]
KCU
- Impact strength , [ kJ / m2]
HB
- Brinell hardness , [MPa]
Weldability :
without limitations
- welding is done without heating and subsequent heat treeting
limited weldability
- welding is possible under heating up to 100-120 grade and subsequent heat treeting
hard weldability
- obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal trader