Metals -> Tool steel -> High speed tool steel Characteristics of the material R9M4K8 ( R9M4K8, Ð9Ì4Ê8 ).
Material : R9M4K8 ( R9M4K8, Ð9Ì4Ê8 ) Classification : High speed tool steel
Chemical composition in % of the material R9M4K8 ( R9M4K8, Ð9Ì4Ê8 ) . C Si Mn Ni S P Cr Mo W V Co 1 - 1.1 max 0.5 max 0.5 max 0.4 max 0.03 max 0.03 3 - 3.6 3.8 - 4.3 8.5 - 9.5 2.3 - 2.7 7.5 - 8.5
Temperature of critical points of the grade R9M4K8 ( R9M4K8, Ð9Ì4Ê8 ).
Ac1 = 800 , Ac3 (Acm ) = 840 , Ar3 (Arcm ) = 790 , Ar1 = 750
Mechanical properties under Ò=20o Ñ of the material R9M4K8 ( R9M4K8, Ð9Ì4Ê8 ) .
Assortment
Dimension
Direct.
s â
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - 960 540 7 10 80 As-delivered state
Brinell hardness of the material R9M4K8 ( R9M4K8, Ð9Ì4Ê8 ) (annealing) , HB 10 -1 = 285 MPa
Physical properties of the material R9M4K8 ( R9M4K8, Ð9Ì4Ê8 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 2.29 8300 100 25 200 27 300 28 400 29 500 30 600 31 700 32 800 900 32 T E 10- 5 a 10 6 l r C R 10 9
Specification :
Mechanical properties :
s â - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Èíôîðìàöèÿ âçÿòà ñ ñàéòà Ìàðî÷íèê ñòàëè è ñïëàâîâ
© 2002 - 2009 Ìîññïåöñòàëü. Âñå ïðàâà çàùèùåíû