Metals -> Structural steel -> High quality structural carbon steel Characteristics of the material 10 ( 10, 10 ).
Material : 10 ( 10, 10 ) Substitute: 08, 15, 08кп Classification : High quality structural carbon steel
Chemical composition in % of the material 10 ( 10, 10 ) . C Si Mn Ni S P Cr Cu As 0.07 - 0.14 0.17 - 0.37 0.35 - 0.65 max 0.25 max 0.04 max 0.035 max 0.15 max 0.25 max 0.08
Temperature of critical points of the grade 10 ( 10, 10 ).
Ac1 = 724 , Ac3 (Acm ) = 876 , Ar3 (Arcm ) = 850 , Ar1 = 682
Mechanical properties under Т=20o С of the material 10 ( 10, 10 ) .
Assortment
Dimension
Direct.
s в
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - Bar hotrolled to Ж 80 340 210 30 55 Sheet hotrolled to 4 300 24 Sheet cold-rolled to 4 300 24 Sheet to 60 340 32 Normalizing Pipe cold-rolled 340 200 26 Normalizing Pipe hotrolled 360 240 25
Brinell hardness of the material 10 ( 10, 10 ) (hot-rolled) , HB 10 -1 = 143 MPa Brinell hardness of the material 10 ( 10, 10 ) (cold-drawn, cold-worked) , HB 10 -1 = 187 MPa
Physical properties of the material 10 ( 10, 10 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 2.1 7856 140 100 2.03 12.4 57 7832 494 190 200 1.99 13.2 53 7800 532 263 300 1.9 13.9 49.6 7765 565 352 400 1.82 14.5 45 7730 611 458 500 1.72 14.85 39.9 7692 682 584 600 1.6 15.1 35.7 7653 770 734 700 15.2 32 7613 857 905 800 12.05 29 7582 875 1081 900 14.08 27 7594 795 1130 1000 12.6 666 1100 14.4 668 T E 10- 5 a 10 6 l r C R 10 9
Technological properties of the material 10 ( 10, 10 ) . Weldability: without limitations. Flakes : not predisposed Temper brittleness: not predisposed
Specification :
Mechanical properties :
s в - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Weldability :
without limitations - welding is done without heating and subsequent heat treeting
limited weldability - welding is possible under heating up to 100-120 grade and subsequent heat treeting
hard weldability - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Информация взята с сайта Марочник стали и сплавов
© 2002 - 2009 Мосспецсталь. Все права защищены