Metals -> Structural steel -> Alloy structurall steel Characteristics of the material 35KH ( 35H, 35Х ).
Material : 35KH ( 35H, 35Х ) Substitute: 40Х, 35ХР Classification : Alloy structurall steel
Chemical composition in % of the material 35KH ( 35H, 35Х ) . C Si Mn Ni S P Cr Cu 0.31 - 0.39 0.17 - 0.37 0.5 - 0.8 max 0.3 max 0.035 max 0.035 0.8 - 1.1 max 0.3
Temperature of critical points of the grade 35KH ( 35H, 35Х ).
Ac1 = 743 , Ac3 (Acm ) = 782 , Ar3 (Arcm ) = 730 , Ar1 = 693 , Mn = 360
Mechanical properties under Т=20o С of the material 35KH ( 35H, 35Х ) .
Assortment
Dimension
Direct.
s в
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - Forging to 100 655 490 16 45 590 Guenching and drawing Forging 100 - 300 615 395 15 40 540 Guenching and drawing Bar Ж 25 910 735 11 45 690 Guenching 860o C, oil, Drawing 500o C, water,
Brinell hardness of the material 35KH ( 35H, 35Х ) (annealing) , HB 10 -1 = 197 MPa Brinell hardness of the material 35KH ( 35H, 35Х ) (cold-drawn, cold-worked) , HB 10 -1 = 207 MPa
Physical properties of the material 35KH ( 35H, 35Х ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 2.14 100 11.3 47 200 12 43 300 2.07 12.9 40 400 13.7 36 500 1.76 14.2 600 14.6 T E 10- 5 a 10 6 l r C R 10 9
Technological properties of the material 35KH ( 35H, 35Х ) . Weldability: limited weldability. Flakes : weakly predisposed Temper brittleness: predisposed
Specification :
Mechanical properties :
s в - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Weldability :
without limitations - welding is done without heating and subsequent heat treeting
limited weldability - welding is possible under heating up to 100-120 grade and subsequent heat treeting
hard weldability - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Информация взята с сайта Марочник стали и сплавов
© 2002 - 2009 Мосспецсталь. Все права защищены