Metals -> High-temperature or heat-resistant steel and alloy -> High alloy high-temperature steel Characteristics of the material 08KH16N13M2B ( 08H16N13M2B, 08Х16Н13М2Б ).
Material : 08KH16N13M2B ( 08H16N13M2B, 08Х16Н13М2Б ) Classification : High alloy high-temperature steel
Chemical composition in % of the material 08KH16N13M2B ( 08H16N13M2B, 08Х16Н13М2Б ) . C Si Mn Ni S P Cr Mo Nb 0.06 - 0.12 max 0.8 max 1 12.5 - 14.5 max 0.02 max 0.035 15 - 17 2 - 2.5 0.9 - 1.3
Mechanical properties under Т=20o С of the material 08KH16N13M2B ( 08H16N13M2B, 08Х16Н13М2Б ) .
Assortment
Dimension
Direct.
s в
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - Bar longitudinal 560 220 40 50 1200 Guenching 1100 - 1130o C, air, Sheet dihedral 550 230 25 800 Guenching 1000 - 1080o C, water,
Brinell hardness of the material 08KH16N13M2B ( 08H16N13M2B, 08Х16Н13М2Б ) (annealing) , HB 10 -1 = 143 - 179 MPa
Physical properties of the material 08KH16N13M2B ( 08H16N13M2B, 08Х16Н13М2Б ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 2.06 7960 100 2 15.2 200 1.91 17.1 300 1.83 18.4 400 1.74 17.1 20.1 500 1.67 17.4 21.7 600 1.58 17.8 23 700 18.2 24.7 800 18.6 T E 10- 5 a 10 6 l r C R 10 9
Specification :
Mechanical properties :
s в - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Информация взята с сайта Марочник стали и сплавов
© 2002 - 2009 Мосспецсталь. Все права защищены