Metals -> Structural steel -> Alloy structurall steel Characteristics of the material 36KH2N2MFÀ ( 36H2N2MFÀ, 36Õ2Í2ÌÔÀ ).
Material : 36KH2N2MFÀ ( 36H2N2MFÀ, 36Õ2Í2ÌÔÀ ) Substitute: 37ÕÍ3ÌÔÀ Classification : Alloy structurall steel
Chemical composition in % of the material 36KH2N2MFÀ ( 36H2N2MFÀ, 36Õ2Í2ÌÔÀ ) . C Si Mn Ni S P Cr Mo V Cu 0.33 - 0.4 0.17 - 0.37 0.25 - 0.5 1.3 - 1.7 max 0.025 max 0.025 1.3 - 1.7 0.3 - 0.4 0.1 - 0.18 max 0.3
Temperature of critical points of the grade 36KH2N2MFÀ ( 36H2N2MFÀ, 36Õ2Í2ÌÔÀ ).
Ac1 = 740 , Ac3 (Acm ) = 780 , Ar3 (Arcm ) = 400 , Ar1 = 300
Mechanical properties under Ò=20o Ñ of the material 36KH2N2MFÀ ( 36H2N2MFÀ, 36Õ2Í2ÌÔÀ ) .
Assortment
Dimension
Direct.
s â
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - Bar Æ 25 1180 1080 12 50 780 Guenching and drawing
Brinell hardness of the material 36KH2N2MFÀ ( 36H2N2MFÀ, 36Õ2Í2ÌÔÀ ) (annealing) , HB 10 -1 = 269 MPa
Physical properties of the material 36KH2N2MFÀ ( 36H2N2MFÀ, 36Õ2Í2ÌÔÀ ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 2.12 36 278 100 2.04 12.5 36 496 335 200 1.98 12.8 35 508 432 300 1.86 13.3 35 525 517 400 1.73 13.5 34 538 613 500 1.66 14 33 567 720 600 1.56 14.3 31 601 825 700 1.39 14.5 30 672 940 800 1.27 11 29 697 T E 10- 5 a 10 6 l r C R 10 9
Technological properties of the material 36KH2N2MFÀ ( 36H2N2MFÀ, 36Õ2Í2ÌÔÀ ) . Weldability: hard weldability. Flakes : predisposed Temper brittleness: not predisposed
Specification :
Mechanical properties :
s â - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Weldability :
without limitations - welding is done without heating and subsequent heat treeting
limited weldability - welding is possible under heating up to 100-120 grade and subsequent heat treeting
hard weldability - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Èíôîðìàöèÿ âçÿòà ñ ñàéòà Ìàðî÷íèê ñòàëè è ñïëàâîâ
© 2002 - 2009 Ìîññïåöñòàëü. Âñå ïðàâà çàùèùåíû