Characteristics of the material 30KHN3M2FА ( 30HN3M2FА, 30ХН3М2ФА ).
Material :
30KHN3M2FА ( 30HN3M2FА, 30ХН3М2ФА )
Classification :
Alloy structurall steel
Chemical composition in % of the material 30KHN3M2FА ( 30HN3M2FА, 30ХН3М2ФА ) .
C
Si
Mn
Ni
S
P
Cr
Mo
V
Cu
0.26 - 0.32
max 0.37
0.2 - 0.5
3 - 3.5
max 0.022
max 0.025
1.2 - 1.7
0.4 - 0.65
0.1 - 0.2
max 0.25
Temperature of critical points of the grade 30KHN3M2FА ( 30HN3M2FА, 30ХН3М2ФА ).
Ac1 = 725 , Ac3(Acm) = 800
Mechanical properties under Т=20oС of the material 30KHN3M2FА ( 30HN3M2FА, 30ХН3М2ФА ) .
Assortment
Dimension
Direct.
sв
sT
d5
y
KCU
Heat treatment
-
mm
-
MPa
MPa
%
%
kJ / m2
-
Forging
to 500
900
750
12
35
500
Guenching 850 - 870oC,Drawing 580 - 650oC,
Brinell hardness of the material 30KHN3M2FА ( 30HN3M2FА, 30ХН3М2ФА ) (quenching, tempering) ,
HB 10 -1= 277 - 321 MPa
Technological properties of the material 30KHN3M2FА ( 30HN3M2FА, 30ХН3М2ФА ) .
Weldability:
hard weldability.
Flakes :
predisposed
Temper brittleness:
weakly predisposed
Specification :
Mechanical properties :
sв
- Tensile strength , [MPa]
sT
- Yield stress, [MPa]
d5
- Specific elongation at fracture , [ % ]
y
- Reduction of area , [ % ]
KCU
- Impact strength , [ kJ / m2]
HB
- Brinell hardness , [MPa]
Weldability :
without limitations
- welding is done without heating and subsequent heat treeting
limited weldability
- welding is possible under heating up to 100-120 grade and subsequent heat treeting
hard weldability
- obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal trader