Metals -> Structural steel -> Alloy structurall steel Characteristics of the material 12KHN2 ( 12HN2, 12ÕÍ2 ).
Material : 12KHN2 ( 12HN2, 12ÕÍ2 ) Substitute: 20ÕÍÐ, 20ÕÃÍÐ, 12ÕÍ3À, 18ÕÃÒ, 20ÕÃÐ Classification : Alloy structurall steel
Chemical composition in % of the material 12KHN2 ( 12HN2, 12ÕÍ2 ) . C Si Mn Ni S P Cr Cu 0.09 - 0.16 0.17 - 0.37 0.3 - 0.6 1.5 - 1.9 max 0.035 max 0.035 0.6 - 0.9 max 0.3
Temperature of critical points of the grade 12KHN2 ( 12HN2, 12ÕÍ2 ).
Ac1 = 715 , Ac3 (Acm ) = 773 , Ar3 (Arcm ) = 726 , Ar1 = 659 , Mn = 405
Mechanical properties under Ò=20o Ñ of the material 12KHN2 ( 12HN2, 12ÕÍ2 ) .
Assortment
Dimension
Direct.
s â
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - Steel 30 Ö 550 420 29 79 3630 Guenching 880o C, oil, Drawing 600o C, water, Steel 30 Ö 550 420 29 79 3630 Guenching 880o C, oil, Drawing 600o C, water, Bar Æ 15 800 600 12 50
Brinell hardness of the material 12KHN2 ( 12HN2, 12ÕÍ2 ) (annealing) , HB 10 -1 = 207 MPa
Physical properties of the material 12KHN2 ( 12HN2, 12ÕÍ2 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 2.11 38 7880 330 100 2.03 10.5 38 494 360 200 1.96 11.5 37 507 430 300 1.9 11.9 35 523 520 400 1.76 12.4 33 536 590 500 1.72 12.9 31 565 670 600 1.54 13.6 30 586 700 1.41 13.9 29 624 800 1.3 11.7 29 703 1050 900 1120 T E 10- 5 a 10 6 l r C R 10 9
Technological properties of the material 12KHN2 ( 12HN2, 12ÕÍ2 ) . Weldability: limited weldability. Flakes : not predisposed Temper brittleness: predisposed
Specification :
Mechanical properties :
s â - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Weldability :
without limitations - welding is done without heating and subsequent heat treeting
limited weldability - welding is possible under heating up to 100-120 grade and subsequent heat treeting
hard weldability - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Èíôîðìàöèÿ âçÿòà ñ ñàéòà Ìàðî÷íèê ñòàëè è ñïëàâîâ
© 2002 - 2009 Ìîññïåöñòàëü. Âñå ïðàâà çàùèùåíû