Metals -> Copper-zinc alloy (latten, brass) -> Copper-zinc alloys pressure treated Characteristics of the material L59 ( L59, Л59 ).
Material : L59 ( L59, Л59 ) Classification : Copper-zinc alloys pressure treated
Chemical composition in % of the material L59 ( L59, Л59 ) . Fe P Cu As Pb Zn Sb Bi Sn Impurity 39.48 - 43 max 0.01 57 - 60 max 0.01 max 0.5 39.1 - 43 max 0.01 max 0.003 max 0.2 all 0.9
Comment: Zn is a basis; the percentage of Zn is given approximately. Mechanical properties under Т=20o С of the material L59 ( L59, Л59 ) .
Assortment
Dimension
Direct.
s в
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - soft 390 44 62 hard 500 10 40
Brinell hardness of the material L59 ( L59, Л59 ) , casted HB 10 -1 = 77 MPa Brinell hardness of the material L59 ( L59, Л59 ) , hard HB 10 -1 = 163 MPa
Physical properties of the material L59 ( L59, Л59 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 21 126 8400
Friction coefficient of the material L59 ( L59, Л59 ) . Friction coefficient with oil
: 0.012 Friction coefficient without oil
: 0.45
Technological properties of the material L59 ( L59, Л59 ) . Forging temperature,°C : 730 - 820 Casting temperature, °C : 1030 - 1080 Linear shrinkage, % : 1.97
Specification :
Mechanical properties :
s в - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Информация взята с сайта Марочник стали и сплавов
© 2002 - 2009 Мосспецсталь. Все права защищены