Metals -> High-temperature or heat-resistant steel and alloy -> High alloy high-temperature steel Characteristics of the material 18KH12VMBFR ( 18H12VMBFR, 18Õ12ÂÌÁÔÐ ).
Material : 18KH12VMBFR ( 18H12VMBFR, 18Õ12ÂÌÁÔÐ ) Classification : High alloy high-temperature steel
Chemical composition in % of the material 18KH12VMBFR ( 18H12VMBFR, 18Õ12ÂÌÁÔÐ ) . C Si Mn Ni S P Cr Mo W V Nb B 0.15 - 0.22 max 0.5 max 0.5 max 0.06 max 0.025 max 0.03 11 - 13 0.4 - 0.6 0.4 - 0.7 0.15 - 0.18 0.2 - 0.4 max 0.003
Temperature of critical points of the grade 18KH12VMBFR ( 18H12VMBFR, 18Õ12ÂÌÁÔÐ ).
Ac1 = 850 , Ac3 (Acm ) = 930
Mechanical properties under Ò=20o Ñ of the material 18KH12VMBFR ( 18H12VMBFR, 18Õ12ÂÌÁÔÐ ) .
Assortment
Dimension
Direct.
s â
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - Pipe Æ 30 x 6 dihedral 820 640 17 56 900 Normalizing 1050o C,Cooling air, Drawing 750o C, 3h,Cooling air, Pipe Æ 219 x 27 dihedral 750 590 15 43 400 Normalizing 1050o C,Cooling air, Drawing 750o C, 3h,Cooling air, Bars 60 740 490 12 45 390 Guenching and drawing
Brinell hardness of the material 18KH12VMBFR ( 18H12VMBFR, 18Õ12ÂÌÁÔÐ ) (annealing) , HB 10 -1 = 229 MPa
Physical properties of the material 18KH12VMBFR ( 18H12VMBFR, 18Õ12ÂÌÁÔÐ ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 2.28 27.6 7850 100 11.15 21.8 200 2.15 11.13 24 300 2.09 11.42 25.1 400 1.95 11.8 26.3 500 1.88 12 27.2 600 1.73 12.5 28 700 1.55 12.65 28.9 800 11.6 T E 10- 5 a 10 6 l r C R 10 9
Technological properties of the material 18KH12VMBFR ( 18H12VMBFR, 18Õ12ÂÌÁÔÐ ) . Weldability: is not used.
Specification :
Mechanical properties :
s â - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Weldability :
without limitations - welding is done without heating and subsequent heat treeting
limited weldability - welding is possible under heating up to 100-120 grade and subsequent heat treeting
hard weldability - obtaining the quality welding needs the additional operations:heating up to 200-300 grade; the heat treeting ia annealing
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Èíôîðìàöèÿ âçÿòà ñ ñàéòà Ìàðî÷íèê ñòàëè è ñïëàâîâ
© 2002 - 2009 Ìîññïåöñòàëü. Âñå ïðàâà çàùèùåíû