Metals -> Copper -> High-temperature cooper alloy Characteristics of the material Cu ( Cu, Cu ).
Material : Cu ( Cu, Cu ) Classification : High-temperature cooper alloy
Comment: Cu is a basis; the percentage of Cu is given approximately. Mechanical properties under Т=20o С of the material Cu ( Cu, Cu ) .
Assortment
Dimension
Direct.
s в
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - 245 157 50 90 1666
Brinell hardness of the material Cu ( Cu, Cu ) , deformed HB 10 -1 = 100 MPa Brinell hardness of the material Cu ( Cu, Cu ) , annealed HB 10 -1 = 45 MPa
Physical properties of the material Cu ( Cu, Cu ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 1.29 16.8 394 8940 17.2
Technological properties of the material Cu ( Cu, Cu ) . Melting temperature, °C : 1083 Forging temperature,°C : 800 - 950 Annealing temperature, °C : 500 - 700
Specification :
Mechanical properties :
s в - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Информация взята с сайта Марочник стали и сплавов
© 2002 - 2009 Мосспецсталь. Все права защищены