Metals -> Tin -> Tin Characteristics of the material O1pch ( О1пч ).
Material : O1pch ( О1пч ) Classification : Tin
Chemical composition in % of the material O1pch ( О1пч ) . Fe S Cu As Pb Sb Bi Sn Impurity max 0.009 max 0.01 max 0.01 max 0.01 max 0.025 max 0.015 max 0.01 min 99.915 all 0.085
Comment: Sn is a basis; the percentage of Sn is given approximately. Mechanical properties under Т=20o С of the material O1pch ( О1пч ) .
Assortment
Dimension
Direct.
s в
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - casted 19-21 45-60
Brinell hardness of the material O1pch ( О1пч ) , casted HB 10 -1 = 4.9 - 5.2 MPa
Physical properties of the material O1pch ( О1пч ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 0.55 7300 100 2.3
Technological properties of the material O1pch ( О1пч ) . Melting temperature, °C : 231.9
Specification :
Mechanical properties :
s в - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Информация взята с сайта Марочник стали и сплавов
© 2002 - 2009 Мосспецсталь. Все права защищены