Metals -> Bronze -> Tin foundry bronzes Characteristics of the material BrO8N4TS2 ( BrO8N4TS2, ÁðÎ8Í4Ö2 ).
Material : BrO8N4TS2 ( BrO8N4TS2, ÁðÎ8Í4Ö2 ) Classification : Tin foundry bronzes
Comment: Cu is a basis; the percentage of Cu is given approximately. Mechanical properties under Ò=20o Ñ of the material BrO8N4TS2 ( BrO8N4TS2, ÁðÎ8Í4Ö2 ) .
Assortment
Dimension
Direct.
s â
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - sand (mould) casting 265 175 14 cast in a metal mould 345 16
Brinell hardness of the material BrO8N4TS2 ( BrO8N4TS2, ÁðÎ8Í4Ö2 ) , HB 10 -1 = 78.5 MPa
Physical properties of the material BrO8N4TS2 ( BrO8N4TS2, ÁðÎ8Í4Ö2 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 17.61 8860
Technological properties of the material BrO8N4TS2 ( BrO8N4TS2, ÁðÎ8Í4Ö2 ) . Melting temperature, °C : 810
Specification :
Mechanical properties :
s â - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Èíôîðìàöèÿ âçÿòà ñ ñàéòà Ìàðî÷íèê ñòàëè è ñïëàâîâ
© 2002 - 2009 Ìîññïåöñòàëü. Âñå ïðàâà çàùèùåíû