Metals -> Magnesium -> Wrought magnesium Characteristics of the material MА14 ( МА14 ).
Material : MА14 ( МА14 ) Classification : Wrought magnesium
Chemical composition in % of the material MА14 ( МА14 ) . Zr Mg Zn 0.3 - 0.9 93.1 - 94.7 5 - 6
Comment: Mg is a basis; the percentage of Mg is given approximately. Mechanical properties under Т=20o С of the material MА14 ( МА14 ) .
Assortment
Dimension
Direct.
s в
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - 320-340 220-290 6-14 60
Brinell hardness of the material MА14 ( МА14 ) , HB 10 -1 = 60 MPa
Physical properties of the material MА14 ( МА14 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 0.42 117.2 1800 56 100 20.9 1046.7 200 26 T E 10- 5 a 10 6 l r C R 10 9
Technological properties of the material MА14 ( МА14 ) . Linear shrinkage, % : 3.2
Specification :
Mechanical properties :
s в - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Информация взята с сайта Марочник стали и сплавов
© 2002 - 2009 Мосспецсталь. Все права защищены