Metals -> Copper -> Copper-nickel alloys Characteristics of the material MNZHMts30-1-1 ( MNZHMts30-1-1, ÌÍÆÌö30-1-1 ).
Material : MNZHMts30-1-1 ( MNZHMts30-1-1, ÌÍÆÌö30-1-1 ) Classification : Copper-nickel alloys
Chemical composition in % of the material MNZHMts30-1-1 ( MNZHMts30-1-1, ÌÍÆÌö30-1-1 ) . Ni+Co Fe C Si Mn S P Cu Pb Zn Impurity 29 - 33 0.5 - 1 max 0.05 max 0.15 0.5 - 1 max 0.01 max 0.006 64.4 - 70 max 0.05 max 0.5 all 0.6
Comment: Cu is a basis; the percentage of Cu is given approximately. Mechanical properties under Ò=20o Ñ of the material MNZHMts30-1-1 ( MNZHMts30-1-1, ÌÍÆÌö30-1-1 ) .
Assortment Dimension Direct. s â s T
d 5
y KCU Heat treatment - mm - MPa MPa % % kJ / m2 - soft 350-450 40-50 hard 550-650 3-5
Brinell hardness of the material MNZHMts30-1-1 ( MNZHMts30-1-1, ÌÍÆÌö30-1-1 ) , soft HB 10 -1 = 58.8 - 68.9 MPa Brinell hardness of the material MNZHMts30-1-1 ( MNZHMts30-1-1, ÌÍÆÌö30-1-1 ) , hard HB 10 -1 = 98 MPa
Physical properties of the material MNZHMts30-1-1 ( MNZHMts30-1-1, ÌÍÆÌö30-1-1 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 1.45 37 8900 420 100 16
Technological properties of the material MNZHMts30-1-1 ( MNZHMts30-1-1, ÌÍÆÌö30-1-1 ) . Melting temperature, °C : 1230 Forging temperature,°C : 860 - 950 Annealing temperature, °C : 750 - 810
Specification :
Mechanical properties : s â - Tensile strength , [MPa] s T - Yield stress, [MPa] d 5 - Specific elongation at fracture , [ % ] y - Reduction of area , [ % ] KCU - Impact strength , [ kJ / m2 ] HB - Brinell hardness , [MPa]
Physical properties : T - Test temperature , [Grade] E - Young modulus , [MPa] a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade] l - Termal (heat) condition coefficient , [Watt/(m·Grade)] r - Density , [kg/m3 ] C - Specific heat
( range 20o - T ), [J/(kg·Grade)] R - Electrical resistance , [Ohm·m]