Metals -> Copper -> Copper Characteristics of the material M00b ( M00b, М00б ).
Material : M00b ( M00b, М00б ) Classification : Copper
Chemical composition in % of the material M00b ( M00b, М00б ) . Fe Ni S P Cu As Pb Zn Ag O Sb Bi Sn max 0.001 max 0.001 max 0.001 max 0.0003 min 99.99 max 0.001 max 0.001 max 0.0001 max 0.002 max 0.001 max 0.001 max 0.0005 max 0.001
Mechanical properties under Т=20o С of the material M00b ( M00b, М00б ) .
Assortment
Dimension
Direct.
s в
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - soft 200-250 90-150 60 hard 400-490 300-450 6
Brinell hardness of the material M00b ( M00b, М00б ) , soft HB 10 -1 = 45 MPa Brinell hardness of the material M00b ( M00b, М00б ) , hard HB 10 -1 = 110 MPa
Physical properties of the material M00b ( M00b, М00б ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 1.28 387 8940 390 17.8 100 1.32 16.7
Technological properties of the material M00b ( M00b, М00б ) . Melting temperature, °C : 1083 Casting temperature, °C : 1150 - 1250 Linear shrinkage, % : 2.1
Specification :
Mechanical properties :
s в - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Информация взята с сайта Марочник стали и сплавов
© 2002 - 2009 Мосспецсталь. Все права защищены