Metals -> Aluminium alloy -> Alluminium antifriction alloys Characteristics of the material ÀO6-1 ( ÀO6-1, ÀÎ6-1 ).
Material : ÀO6-1 ( ÀO6-1, ÀÎ6-1 ) Classification : Alluminium antifriction alloys
Chemical composition in % of the material ÀO6-1 ( ÀO6-1, ÀÎ6-1 ) . Fe Si Ni Al Cu Sn Impurity max 0.3 max 0.3 0.7 - 1.3 89.5 - 93.6 0.7 - 1.3 5 - 7 other 0.3
Comment: Al is a basis; the percentage of Al is given approximately. Mechanical properties under Ò=20o Ñ of the material ÀO6-1 ( ÀO6-1, ÀÎ6-1 ) .
Assortment
Dimension
Direct.
s â
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - cast in a metal mould 160 80 12
Brinell hardness of the material ÀO6-1 ( ÀO6-1, ÀÎ6-1 ) , cast in a metal mould HB 10 -1 = 45 MPa
Physical properties of the material ÀO6-1 ( ÀO6-1, ÀÎ6-1 ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 0.724 23.4 180 2880
Limiting operating condition of the material ÀO6-1 ( ÀO6-1, ÀÎ6-1 )
Load Speed Load * Speed Temperature
MPa m/s MPa * m/s Grade
31.2 20 120
Technological properties of the material ÀO6-1 ( ÀO6-1, ÀÎ6-1 ) . Melting temperature, °C : 224 - 649
Specification :
Mechanical properties :
s â - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Èíôîðìàöèÿ âçÿòà ñ ñàéòà Ìàðî÷íèê ñòàëè è ñïëàâîâ
© 2002 - 2009 Ìîññïåöñòàëü. Âñå ïðàâà çàùèùåíû