Metals -> Copper-zinc alloy (latten, brass) -> Cast cooper-zinc alloys Characteristics of the material LTS40S ( LTS40S, ËÖ40Ñ ).
Material : LTS40S ( LTS40S, ËÖ40Ñ ) Classification : Cast cooper-zinc alloys
Chemical composition in % of the material LTS40S ( LTS40S, ËÖ40Ñ ) . Fe Si Mn Ni Al Cu Pb Zn Sb Sn Impurity max 0.8 max 0.3 max 0.5 max 1 max 0.5 57 - 61 0.8 - 2 35 - 42.2 max 0.05 max 0.5 all 2
Comment: Zn is a basis; the percentage of Zn is given approximately. Mechanical properties under Ò=20o Ñ of the material LTS40S ( LTS40S, ËÖ40Ñ ) .
Assortment
Dimension
Direct.
s â
s T
d 5
y
KCU
Heat treatment - mm - MPa MPa % % kJ / m2 - sand (mould) casting 215 12 cast in a metal mould 215 20 centrifugal casting 215 20
Brinell hardness of the material LTS40S ( LTS40S, ËÖ40Ñ ) , sand (mould) casting HB 10 -1 = 70 MPa Brinell hardness of the material LTS40S ( LTS40S, ËÖ40Ñ ) , cast in a metal mould HB 10 -1 = 80 MPa Brinell hardness of the material LTS40S ( LTS40S, ËÖ40Ñ ) , centrifugal casting HB 10 -1 = 80 MPa
Physical properties of the material LTS40S ( LTS40S, ËÖ40Ñ ) . T E 10- 5 a 10 6 l r C R 10 9 Grade MPa 1/Grade Watt/(m·Grade) kg/m3 J/(kg·Grade) Ohm·m 20 20.1 108.8 8500 68
Friction coefficient of the material LTS40S ( LTS40S, ËÖ40Ñ ) . Friction coefficient with oil
: 0.013 Friction coefficient without oil
: 0.17
Technological properties of the material LTS40S ( LTS40S, ËÖ40Ñ ) . Melting temperature, °C : 885
Specification :
Mechanical properties :
s â - Tensile strength , [MPa]
s T - Yield stress, [MPa]
d 5 - Specific elongation at fracture , [ % ]
y - Reduction of area , [ % ]
KCU - Impact strength , [ kJ / m2 ]
HB - Brinell hardness , [MPa]
Physical properties :
T - Test temperature , [Grade]
E - Young modulus , [MPa]
a - Coefficient of linear expansion
(range 20o - T ) , [1/Grade]
l - Termal (heat) condition coefficient , [Watt/(m·Grade)]
r - Density , [kg/m3 ]
C - Specific heat
( range 20o - T ), [J/(kg·Grade)]
R - Electrical resistance , [Ohm·m]
Database of steels and alloys (Marochnik) contains information about chemical composition and properties of 1500 steels and alloys (stainless steel, alloy steel, carbone steel, structural steel, tool steel, cast iron, aluminum alloy, titanium alloy, copper alloy, nickel alloy, magnesium alloy and others). Helpfull for specialists in material technology, structural engineer, mechanical engineer, metallurgy and metal traderTop
© 2003 - 2009 All rights reserved. About program.
The entire risk as to use of the Database of Steel and Alloy (Marochnik) content is assumed by you the user
Èíôîðìàöèÿ âçÿòà ñ ñàéòà Ìàðî÷íèê ñòàëè è ñïëàâîâ
© 2002 - 2009 Ìîññïåöñòàëü. Âñå ïðàâà çàùèùåíû